| 厂家(产地)：韩国锦湖 | 牌号：HI-450 | 加工级别：注塑级 |
| 特性级别：耐磨 | 销售方式：品牌经销 | 类型：标准料 |
龙创供应现货韩国锦湖HIPS HI-450,耐磨级HIPS
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 4.0 | g/10min |
| 模具收缩率 | Flow | ASTM D-955 | 0.30-0.60 | % | |
| 吸水率 | 24hr | ASTM D-570 | 0.050 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
| 机械性能 | 拉伸屈服强度 | ASTM D-638 | 40.1 | MPa | |
| 拉伸屈服伸长率 | ASTM D-638 | 45 | % | ||
| 弯曲模量 | ASTM D-790 | 2250 | MPa | ||
| 弯曲屈服强度 | ASTM D-790 | 43.1 | MPa | ||
| IZOD缺口冲击强度 | 3.18mm | ASTM D-256 | 89.1 | J/m | |
| 洛氏硬度 | ASTM D-785 | 80 | L scale | ||
| 电气性能 | 体积电阻率 | ASTM D-257 | 1.0E+16 | ohm.cm | |
| 介电强度 | ASTM D-149 | 17.7 | KV/mm | ||
| 介电常数 | 1E+6Hz | ASTM D-150 | 2.700 | ||
| 热性能 | 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 82.2 | ℃ |
| 维卡软化温度 | ASTM D-1525 | 101 | ℃ | ||
| 燃烧性 | 1.59mm | UL 94 | HB | ||
| 燃烧性 | 3.18mm | UL 94 | HB | ||
| 燃烧性 | 6.35mm | UL 94 | HB | ||
| RTI Str | 1.59mm | UL 746 | 50.0 | ℃ | |
| RTI Str | 3.18mm | UL 746 | 50.0 | ℃ | |
| RTI Str | 6.35mm | UL 746 | 50.0 | ℃ | |
| RTI Imp | 1.59mm | UL 746 | 50.0 | ℃ | |
| RTI Imp | 3.18mm | UL 746 | 50.0 | ℃ | |
| RTI Imp | 6.35mm | UL 746 | 50.0 | ℃ | |
| RTI Elec | 1.59mm | UL 746 | 50.0 | ℃ | |
| RTI Elec | 3.18mm | UL 746 | 50.0 | ℃ | |
| RTI Elec | 6.35mm | UL 746 | 50.0 | ℃ | |
通用级聚苯乙烯是一种热塑性树脂,为无色、无臭、无味而有光泽的、透明的珠状或粒状的固体。电绝
缘性（尤其高频绝缘性）优良，无色透明，透光率仅次于有机玻璃，着色性耐水性，化学稳定性良好，强度
一般，但质脆，易产生应力脆裂，不耐苯、汽油等有机溶剂.适于制作绝缘透明件.装饰件及化学仪器.光学仪
器等零件.
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
| ||||||||||||||||||
|